PA2210 FR

PA2210 FR Datasheet - Flame Retardant Selective Laser Sintering Material

 

PA2210 FR Applications

    • Flame retardant
    • High temperature resistant
    • Suitable for aerospace industry testing – passes 12s burning test at wall thickness of 1.5 and 2mm
    • Suitable for electrical and electronic housingsPA2210FR
 Physical Properties
 Colour White
 Type Flame retardant, high temp. material
Mechanical Properties
 Test/ISO
Flexural Modulus 2300 (MPa)  ISO178
Tensile Modulus (X,Y direction)  2500 (MPa)  ISO 527
Tensile Modulus (Z direction)  2300 (MPa)
Tensile Strength (X,Y direction) 45 (MPa)
Tensile Strength (Z direction) 41 (MPa)
Elongation Break (X,Y direction)  5%
Elongation Break (Z direction) 3%
   Thermal & Scientific Properties
Melting Point 176 °C  ISO 11357
Burning behaviour @ 1.5mm nom. thickness HB Class IEC 60695-11-10
Burning behaviour @ thickness h (2mm) V-0 Class

PA2210 FR Applications

    • Flame retardant
    • High temperature resistant
    • Suitable for aerospace industry testing – passes 12s burning test at wall thickness of 1.5 and 2mm
    • Suitable for electrical and electronic housingsPA2210FR
Physical Properties
Colour White
Type Flame retardant, high temp. material
Mechanical Properties
Flexural Modulus 2300 (MPa) Test/ISO: ISO178
Tensile Modulus (X,Y direction) 2500 (MPa) Test/ISO: ISO 527
Tensile Modulus (Z direction) 2300 (MPa) Test/ISO: ISO 527
Tensile Strength (X,Y direction) 45 (MPa) Test/ISO: ISO 527
Tensile Strength (Z direction) 41 (MPa) Test/ISO: ISO 527
Elongation Break (X,Y direction) 5% Test/ISO:ISO 527
Elongation Break (Z direction) 3% Test/ISO:ISO 527
Thermal & Scientific Properties
Melting Point 176 °C Test/ISO:ISO 11357
Burning behaviour @ 1.5mm nom. thickness HB Class Test/ISO: IEC 60695-11-10
Burning behaviour @ thickness h (2mm) V-0 Class Test/ISO: IEC 60695-11-10

 

 