Ceramax
Ceramax Applications.
| ||
| Physical Properties | ||
| Colour | Opaque White | |
| Type | High Temperature Resin offering excellent abrasion, moisture & thermal resistance | |
| Mechanical Properties | ||
| Test/ISO | ||
| Hardness Shore A/D | 89D | |
| Flexural Strength | 137 – 145 (MPa) | ATSM D790 |
| Flexural Modulus | 8,270 – 8,370 (MPa) | |
| Tensile Modulus | 9,460 – 9,680 (MPa) | ATSM D638 |
| Tensile Strength | 78 – 87 (MPa) | |
| Impact Strength | 14.5 – 17.9 J/m | ATSM D256 |
| Elongation Break (%) | 0.7 – 1.0% | ATSM D638 |
| Thermal & Scientific Properties | ||
| Glass Transition Temperature | 108 – 110°C | DMA, E” |
| Heat Deflection Temp (°C) | ATSM D648 | |
| @66 PSI | 148 °C | |
| @264 PSI | 95°C | |
| @66 PSI w/ thermal postcure | 220°C | |
| Co-efficient of Thermal Expansion | E831-93 | |
| TMA (T<Tg, 25 – 57°C) | 31.1µ/m – °C | |
| TMA (T<Tg, 70 – 200°C) | 87.4µ/m – °C | |
Ceramax Applications.
| ||
| Physical Properties | ||
| Colour | Opaque White | |
| Type | High Temperature Resin offering excellent abrasion, moisture & thermal resistance | |
| Mechanical Properties | ||
| Hardness Shore A/D | 89D | |
| Flexural Strength | 137 – 145 (MPa) | Test/ISO: ATSM D790 |
| Flexural Modulus | 8,270 – 8,370 (MPa) | Test/ISO: ATSM D790 |
| Tensile Modulus | 9,460 – 9,680 (MPa) | Test/ISO: ATSM D638 |
| Tensile Strength | 78 – 87 (MPa) | Test/ISO: ATSM D638 |
| Impact Strength | 14.5 – 17.9 J/m | Test/ISO: ATSM D256 |
| Elongation Break (%) | 0.7 – 1.0% | Test/ISO: ATSM D638 |
| Thermal & Scientific Properties | ||
| Glass Transition Temperature | 108 – 110°C | Test/ISO: DMA, E” |
| Heat Deflection Temp (°C) @66 PSI | 148 °C | Test/ISO: ATSM D648 |
| Heat Deflection Temp (°C) @264 PSI | 95°C | Test/ISO: ATSM D648 |
| Heat Deflection Temp (°C) @66 PSI w/ thermal postcure | 220°C | Test/ISO: ATSM D648 |
| Co-efficient of Thermal Expansion TMA (T<Tg, 25 – 57°C) | 31.1µ/m – °C | Test/ISO: E831-93 |
| Co-efficient of Thermal Expansion TMA (T<Tg, 70 – 200°C) | 87.4µ/m – °C | Test/ISO: E831-93 |
For further information contact our sales team on 028 9070 6940.
Request a Ceramax Quote