Si25
Si25 Applications
| ||
Physical Properties | ||
Colour | White | |
Type | Simulates PP Flexible, good for snap fits. | |
Mechanical Properties | ||
Test/ISO | ||
Hardness Shore A/D | 80D | |
Flexural Strength | 55-58 (MPa) | ATSM D790 |
Flexural Modulus | 1,380 – 1,660 (MPa) | |
Tensile Modulus | 1,590 – 1,660 (MPa) | ATSM D638M |
Tensile Strength | 38 (MPa) | |
Impact Strength | 19-24 J/m | ATSM D256A |
Elongation Break (%) | 13-20% | ATSM D638 |
Thermal & Scientific Properties | ||
Glass Transition Temperature | 60°C | DMA, E” |
Heat Deflection Temp (°C) | ATSM D648-98C | |
@0.46 MPa | 58 – 63 °C | |
@1.81 MPa | 51-55°C | |
Co-efficient of Thermal Expansion | E831-93 | |
TMA (T<Tg, 0-20°C) | 107 x 10-6m/m – °C | |
TMA (T<Tg, 90-150°C) | 151 x 10-6m/m – °C |
Si25 Applications
| ||
Physical Properties | ||
Colour | White | |
Type | Simulates PP Flexible, good for snap fits. | |
Mechanical Properties | ||
Hardness Shore A/D | 80D | |
Flexural Strength | 55-58 (MPa) | Test/ISO: ATSM D790 |
Flexural Modulus | 1,380 – 1,660 (MPa) | |
Tensile Modulus | 1,590 – 1,660 (MPa) | Test/ISO: ATSM D638M |
Tensile Strength | 38 (MPa) | |
Impact Strength | 19-24 J/m | Test/ISO: ATSM D256A |
Elongation Break (%) | 13-20% | Test/ISO: ATSM D638 |
Thermal & Scientific Properties | ||
Glass Transition Temperature | 60°C | Test/ISO: DMA, E” |
Heat Deflection Temp (°C) @0.46 MPa | 58 – 63 °C | Test/ISO: ATSM D648-98C |
Heat Deflection Temp (°C) @1.81 MPa | 51-55°C | Test/ISO: ATSM D648-98C |
Co-efficient of Thermal Expansion TMA (T<Tg, 0-20°C) | 107 x 10-6m/m – °C | Test/ISO: E831-93 |
Co-efficient of Thermal Expansion TMA (T<Tg, 90-150°C) | 151 x 10-6m/m – °C | Test/ISO: E831-93 |