SL7820

SL7820 Datasheet - Black Stereolithography Material simulating ABS

SL7820 Applications

 

    • Black parts with high strength & good dimensional stability (even in humid conditions
    • ABS like, fine detailed surfaces
    • Ideal for building
      • Automotive parts
      • Consumer goods
      • Packaging
      • Electronics
      • Housings
      • Toys…
 Physical Properties
 ColourBlack
 TypeSimulates ABS
– First white to black resin with good surface finish detail & excellent dimensional stability
Mechanical Properties
 Test/ISO
Shore Hardness A/D86D ATSM D2240
Flexural Strength59 – 80 (MPa) ATSM D790
Flexural Modulus2,000 – 2,400 (MPa)
Tensile Modulus 1,900 – 2,400 (MPa) ATSM D638M
Tensile Strength36 – 51 (MPa)
Impact Strength 42 – 42 J/mATSM D256A
Elongation Break (%) 6 – 16% ATSM D638
   Thermal & Scientific Properties
Glass Transition Temperature 62°CDMA, E”
Heat Deflection Temp. (°C)ATSM D648-98C
   @66 PSI51°C
Co-efficient of Thermal ExpansionASTM E831-93
93 x 10-6m/m – °C

SL7820 Applications

 

    • Black parts with high strength & good dimensional stability (even in humid conditions
    • ABS like, fine detailed surfaces
    • Ideal for building
      • Automotive parts
      • Consumer goods
      • Packaging
      • Electronics
      • Housings
      • Toys…
Physical Properties
ColourBlack
TypeSimulates ABS
– First white to black resin with good surface finish detail & excellent dimensional stability
Mechanical Properties
Shore Hardness A/D86DTest/ISO: ATSM D2240
Flexural Strength59 – 80 (MPa)Test/ISO: ATSM D790
Flexural Modulus2,000 – 2,400 (MPa)Test/ISO: ATSM D790
Tensile Modulus 1,900 – 2,400 (MPa)Test/ISO: ATSM D638M
Tensile Strength36 – 51 (MPa)Test/ISO: ATSM D638M
Impact Strength 42 – 42 J/mTest/ISO: ATSM D256A
Elongation Break (%) 6 – 16%Test/ISO: ATSM D638
Thermal & Scientific Properties
Glass Transition Temperature 62°CTest/ISO: DMA, E”
Heat Deflection Temp. (°C) @66 PSI51°CTest/ISO: ATSM D648-98C
Co-efficient of Thermal Expansion 93 x 10-6m/m – °CTest/ISO: ASTM E831-93

 

 